Teknologi oven anealling kaca tellurite berbasis mikrokontroller dengan bahan bakar bio-briket

Adi Pramuda, Lia Angraeni, Soka Hadiati

Abstract


The A process known as annealing is important for reducing stress in working optical materials. The problem that arises is that the annealing process requires a large amount of heat energy or total heat. The purpose of this research is to reveal the thermal stability curve of an oven with bio-briquette fuel that works at the average temperature of the annealing process; 2. To obtain the optimal value of the use of bio-briquette fuel at several set temperatures of the tellurite glass annealing process. This research uses laboratory experimental research methods. The results show that: preheating with a time of 8 minutes produces an average oven temperature above the bio-briquette coals of 418 oC. Oven with bio-briquette fuel that works stably at a temperature of 471 oC with a preheating time of 5 minutes; The modification results resulted in the oven's ability to heat stably at 363.6oC for 4 hours using three coconut shell bio-briquettes with a size of 2 x 1.5 x 1.5 cm.


Keywords


Bio-Briquettes, Oven, Anealling, Glass, Arduino

Full Text:

PDF

References


Adhani, L., Masrya, M.A., Octavia, S.I & Sindiany, I.I. (2019). Analisis Bahan Bakar Alternatif Komposit Biobriket dari Eceng Gondok Dengan Perekat Kotoran Sapi. Al-Kimiya, 6(2); 81-86.

Aridito, M. N. & Cahyono, M. S. (2019). Pengaruh laju pemanasan dan laju hisap gas pada proses pirolisis twin retort rocket stove terhadap karakteristik bioarang dari briket limbah serbuk kayu. Makalah disajikan dalam seminar nasional inovasi dan aplikasi teknologi di industri. Institut Teknologi Nasional, Malang, 2 Februari.

Fusari, F. (2011). Continuous wave and modelocked femtosecond novel bulk glass lasers operating around 2000 nm. PhD Tesis tidak diterbitkan. Skotlandia: University of St. Andrews.

Higgins, R. A. (2006). Materials for engineers and technicians. Burlington: Newnes.

Kholilah, I & Al Tahtawi, A. A. (2016). Aplikasi arduino-android untuk sistem keamanan sepeda motor. Jurnal Teknologi Rekayasa, 1 (1): 53-58.

Mallawany, R. E. Dirar, AM. & Ahmed, IA. (2008). New tellurite glass: optical properties. Journal of Materials Chemistry and Physics, 109 (1), 291-296.

Mandasini, Sungkono, Pawennari, A., Ahiruddin. (2016). Analisis Kinerja Tungku Berbahan Bakar Bio-Briket. Journal of Chemical Process Engineering, 01 (01): 25-32.

Pal, B. P. (2006). Guided wave optical components and devices basics technology and applications. Burlington: Elsevier Academic Press.

Rifdah, Herawati, N & Dubron, F. (2017). Pembuatan Biobriket Dari Limbah Tongkol Jagung Pedagang Jagung Rebus dan Rumah Tangga Sebagai Bahan Bakar Energi Terbarukan Dengan Proses Karbonisasi. Distilasi, 2(2): 39-46.

Susanti, P. D., Wahyuningtyas, R. S. & Ardhana, A. (2015). Pemanfaatan gulma lahan gambut sebagai bahan baku bio-briket. Jurnal Penelitian Hasil Hutan, 33 (1): 35-46.

Vachlepi, A & Suwardin, D. (2013). Penggunaan Biobriket Sebagai Bahan Bakar Alternatif dalam Pengeringan Karet Alam. Warta Perkaretan, 32(2), 65 – 73.




DOI: https://doi.org/10.31571/saintek.v11i1.3589

Refbacks

  • There are currently no refbacks.


Copyright (c) 2022 Soka Hadiati, Adi Pramuda, Angraeni Lia

Jurnal Pendidikan Informatika dan Sains

IKIP PGRI Pontianak, Gedung Rektorat Lt. 2
Jl. Ampera No.88, Sungai Jawi, Pontianak Kota, Kota Pontianak, Kalimantan Barat 78116
Telp. (0561) 748219
E-mail: saintek.ikippgriptk@gmail.com 


p-ISSN: 2089-2802 | e-ISSN: 2407-1536


View Stats


Jurnal Pendidikan Informatika dan Sains is licensed under a
Creative Commons License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.